Faiga: Faʻaaogaina i le faʻasolosolo faʻasolosolo i nofoaga maualuga le vevela, lelei le faʻaogaina o le vaivai; Lelei fetuutuunai, faʻafefe i le maualuga o le vevela, faʻasaʻo i le pala; Faʻaaogaina i le suauʻu, alamanuia vailaʻau, aerospace, metallurgy, eletise, kesi, fale, masini. , faufale, u'amea ma u'amea, fai pepa, ie, vaila'au, mea'ai ma va'a ma isi.
Fa'amatalaga lautele:O paipa Capillary o uaea manifinifi e faia i le polytetrafluoroethylene.O paipa Capillary e faʻaaogaina e fai ma auala femalagaiga mo se suʻesuʻega vave ma otometi ina ia maua ai le maualuga maualuga ma le maaleale.O nei paipa e fesoasoani i le fa'atatauina sa'o, fa'aleleia atili le toe gaosia.
Fa'amatalaga:
- * Ole: 0.8 i le 26mm
- *Umi: fa'apitoa
- *Mafiafia: fa'apitoa
- *Maualuluga-maualalo vevela: -270C I LE 260C
- *Tete'e afi:IOE
- *FA'A'OGA: talosaga fa'afoma'i, va'alele, su'esu'ega fa'asaienisi, ma isi fa'aoga mana'omia.
Fa'asinoga Fa'apitoa:
| Aitema | (Metotia Su'ega) | (Fa'amatalaga) |
| (g/cm3)(Lave Fa'apitoa) | ASTM D792 | 2.16 |
| (V)(Value Fa'atatau) | UL-224 | 600V(S)300V(T)150V(L) |
| (℃) UL Fa'atatau Temperature | – | -80~200 |
| (MPa) Malosi Tensile | ASTM D638 | 24.5 |
| (%) Fa'atelega Fa'aumi | ASTM D638 | 350 |
| (MPa)(Flexural Modulus) | ASTM D790 | 490 |
| (A'afiaga Malosi) | ASTM D256+23℃-54℃J/m | -Leai se malologa-107 |
| (Tagata D)(Maaa) | ASTM D2240 | 55 |
| (Coefficient of Dynamic Friction) | – | 0.1 |
| (Fa'asa'o) | – | 327 |
| (Temperature Auaunaga 20000h Faatasi ai ma le 50% Faʻamauina o le Faʻaumiumi Sili) | – | 260 |
| (Mua) | UL-224 | VW-1 |
| (Dielectric Constant I le 103-106Hz) | ASTM D150 | 2.1 |
| (2500V/60s) Malosi Dielectric | UL-224 | IOE |
| (Fa'aliga Fa'aleaogaina ile 106Hz) | ASTM D150 | 0.0002 |
| (S)(Ac Resistance) | ASTM D495 (Electrodes Uamea Uila) | >300 |
| (Ω·cm)(Tete'e Tele) | ASTM D257 | >1018 |
| (Tete'e Tau) | “Tau-O-Meter”(2000h) | Leai se ta'e |
| (Tagata Solvent) | ASTM D543 | Lelei |
| (Tete'e Kemisi) | ASTM D543 | Lelei |
Tele masani:
| AWG | ID(mm) | OD(mm) | afifiina | ||||
| Min | masani | Max | S | T | L | ||
| 30 | 0.25 | 0.3 | 0.38 | 0.7 | 0.76 | 0.6 | 305 |
| 28 | 0.33 | 0.38 | 0.46 | 0.84 | 0.84 | 0.68 | 305 |
| 26 | 0.41 | 0.46 | 0.53 | 0.92 | 0.92 | 0.76 | 305 |
| 24 | 0.51 | 0.56 | 0.66 | 1.16 | 1.06 | 0.86 | 305 |
| 23 | 0.58 | 0.66 | 0.74 | 1.26 | 1.16 | 1.96 | 305 |
| 22 | 0.66 | 0.71 | 0.81 | 1.31 | 1.21 | 1.01 | 305 |
| 21 | 0.74 | 0.81 | 0.89 | 1.41 | 1.31 | 1.11 | 305 |
| 20 | 0.81 | 0.86 | 0.97 | 1.66 | 1.46 | 1.16 | 305 |
| 19 | 0.91 | 0.96 | 1.07 | 1.76 | 1.56 | 1.26 | 305 |
| 18 | 1.01 | 1.07 | 1.17 | 1.87 | 1.67 | 1.37 | 305 |
| 17 | 1.14 | 1.19 | 1.32 | 1.99 | 1.79 | 1.49 | 305 |
| 16 | 1.29 | 1.34 | 1.47 | 2.14 | 1.94 | 1.64 | 305 |
| 15 | 1.45 | 1.5 | 1.65 | 2.3 | 2.1 | 1.8 | 153 |
| 14 | 1.62 | 1.68 | 1.83 | 2.48 | 2.28 | 2.08 | 153 |
| 13 | 1.83 | 1.93 | 2.05 | 2.73 | 2.53 | 2.33 | 153 |
| 12 | 2.05 | 2.16 | 2.31 | 2.96 | 2.77 | 2.56 | 153 |
| 11 | 2.31 | 2.41 | 2.57 | 3.21 | 3.01 | 2.81 | 153 |
| 10 | 2.59 | 2.69 | 2.84 | 3.49 | 3.29 | 3.09 | 153 |
| 9 | 2.9 | 3 | 3.15 | 4 | 3.76 | 3.4 | 100 |
| 8 | 3.28 | 3.38 | 3.53 | 4.38 | 4.14 | 3.78 | 100 |
| 7 | 3.65 | 3.76 | 3.94 | 4.76 | 4.52 | 4.16 | 100 |
| 6 | 4.11 | 4.22 | 4.41 | 5.22 | 4.98 | 4.72 | 100 |
| 5 | 4.62 | 4.72 | 4.95 | 5.72 | 5.48 | 5.22 | 100 |
| 4 | 5.18 | 5.28 | 5.53 | 6.28 | 6.04 | 5.78 | 100 |
| 3 | 5.81 | 5.94 | 6.2 | 6.94 | 6.7 | 6.44 | 100 |
| 2 | 6.55 | 6.68 | 6.93 | 7.68 | 7.44 | 7.18 | 100 |
| 1 | 7.34 | 7.46 | 7.75 | 8.46 | 8.22 | 7.96 | 100 |
| 0 | 8.26 | 8.38 | 8.69 | 9.38 | 9.14 | 8.858 | 100 |